A combined XPS, LEIS and MEIS surface analysis of thermally activated NaSICON inorganic solid electrolytes

In this short video, I present how we used a combination of surface analysis techniques to determine the surface chemical composition of thermally activated NaSICON ceramics. The family of NaSICON material (Na3+xZr2Si2+xP1-xO12, -2

Thanks for watching !