Oxidation of Metals Following Argon Cluster Bombardment

Molecular dynamics was used to aid X-Ray Photoelectron Spectroscopy (XPS) analysis of aluminium, looking into the oxidation of metals after a surface was impacted with various sizes of argon clusters. The results obtained through molecular dynamics allowed the temperature profile of the surface to be modelled. This strongly correlated with results found through XPS analysis.